1. According to the requirements of amount of admixture,add admixture to the mortar,mix with water and stir evenly.The product has no slushing,so mix with water based on the mix proportion.
2. The mortar which is added the ZK-MS wet plastering mortar admixture might affect the drying time in some extent.When the humidity of wall and atmosphere is normal,the construction thickness is within 2cm and the drying time is in accordance with the mixed mortar on site;if the humidity of wall and atmosphere is high or the construction thickness is above 2cm,the drying time is1~3 hours longer than the former;if the humidity of wall and atmosphere is extremely high or the construction thickness is above 2cm,the drying time will belong and we recommend the wall should be splashed wet or add slurry on the thick part in advance and fill in the next day.
3.The sand whose nominal maximum aggyegate size is more than 4.75 should be wiped off and the quantity of silt content should be controlled within 3%.The sand whose silt content are out of limit are forbidden because such sand leads to a large area of ductility crack in mortar.The fineness modulus should range from 2.4 to2.6.
4. Pay attontion to the changes of silt content,degree of thickness and moisture content.The changes of materials may have an influence on the consistence of mortar.
5.When the powder(cement,coal ash and slag powder) in the mortar changes,it should be tested by experimental verification.
6.The consistence of mortar should be between 85cm-95cm and its density should be between 1950~2050Kg/m³.If the mortar is too viscous and it is easy to adhere to the darby.Instead,if not viscous,it is difficult to scrape on the wall.
7.Before the production of mortar,the agitators and tank trucks must keep clean;after production,the agitators and tank trucks should be cleaned.